Quartz glass

Product number：019
sort：Others - Quartz glass

    Our quartz glass optical windows are resistant against high temperature and pressure and can be applied mainly in such fields as special light sources, optical instrument, optical electronics, military equipment, metallurgy, semi-conductor, and optical communications. Their experimental temperature is 1200 degrees and softening temperature 1730 degrees. Detailed parameters are given as follows:
1. JGS1( Extreme UV optical quartz glass)
It is a high-purity optical quartz glass made by oxyhydrogen flame melting. Its satisfactory UV light transmission performance surpass all the other glass types in particular in the shortwave UV zone and can achieve a 90% transmission rate at the wavelength of 185mμ. Hence it is an ideal choice for applications in the wavelength range of 185-2500mμ.
2. JGS2 (UV optical quartz glass)
It is an optical quartz glass made by oxyhydrogen flame melting and is suggested for applications in the wavelength range of 220-2500mμ
3. JGS3 (Infrared quartz glass)
    It has a good performance of infrared light transmission with a transmittance of over 85%. It is recommended for applications in the wavelength range of 260-3500mμ.

Table 1.

Mechanical Property Reference Value Density 2.2g/cm3 Compressive Strength 1100Mpa Bending Strength 67Mpa Tensile Strength 48Mpa Poisson's Ratio 0.14～0.17 Elastic Modulus 72000Mpa Shearing Modulus 31000Mpa Mohs Hardness 5.5～6.5

Table 2.

Mechanical Property Reference Value Deformation Point 1280℃ Softening Point 1780℃ Annealing Point 1250℃ Specific Heat(20～350℃) 670J/kg.℃ Thermal Conductivity(20℃) 1.4W/m.℃ Refractive Index 1.4585 Coefficient of thermal expansion 5.5×10-7cm/cm.℃ Hot work temperature 1750～2050℃ The temperature for a short time 1300℃ The temperature for a long time 1100℃

Table 3.

Electrics Property Reference Value Resistivity 7×107Ω.cm Dielectric Strength 250～400Kv/cm Dielectric Constant 3.7～3.9 Dielectric absorption coefficient <4×104 Dielectric loss coefficient <1×104